17-4PH Pellet

17-4 stainless steel can be heat treated to high levels of strength and hardness, and has a high corrosion resistance compared with 304 stainless steel. 17-4 stainless steel is an ideal material for components which require high hardness and/or corrosion resistance at high temperatures.

17-4PH

17-4PH can be heat treated to high levels of strength and hardness, and has a high corrosion resistance compared with 304 stainless steel. 17-4 stainless steel is an ideal material for components which require high hardness and/or corrosion resistance at high temperatures. It is widely used in petroleum and chemical industries, as well as in aerospace.


Preliminary composition

C

Cr

Ni

Cu

Nb

Mn

Si

Fe

≤0.07

15-17.5%

3-5%

3-5%

0.15-0.45

<1.00

<1.00

Balance

0.05

16.47

3.66

3.91

0.31

0.71

0.72

Balance


Mechanical properties


 As-sintered Uprise 3D

Standard

Density (g/cm3)

>7.6

GB/T 3850-2015

Yield strength (MPa)

650

GB/T 228.1-2010

Tensile strength (MPa)

900

GB/T 228.1-2010

Elongation at break (%)

7

GB/T 228.1-2010

Hardness (HRC)

30

N/A


Nozzle temperature: 150-210oC
Printing speed: 20-60 mm/s
Printing bed temperature: 110-140oC
Chamber temperature: N/A